性能項(xiàng)目
|
試驗(yàn)條件[狀態(tài)]
|
測(cè)試方法
|
測(cè)試數(shù)據(jù)
|
數(shù)據(jù)單位
|
|
熔體流動(dòng)速率
|
ASTM D-1238
|
4
|
g/10min
|
|
|
乙烯基醋酸鹽含量
|
HCC Method
|
28
|
%
|
|
|
密度
|
ASTM D-1505
|
0.95
|
g/cm3
|
|
|
抗張強(qiáng)度(破斷點(diǎn))
|
ASTM D-638
|
190
|
kg/cm2
|
|
|
破斷點(diǎn)伸長(zhǎng)率
|
ASTM D-638
|
800
|
℃
|
|
|
硬度
|
ASTM D-2240
|
79
|
Shore A
|
|
|
硬度
|
ASTM D-2240
|
26
|
Shore D
|
|
|
維卡軟化點(diǎn)
|
ASTM D-1525
|
44
|
℃
|
|
|
熔融點(diǎn)
|
ASTM D-3417
|
75
|
℃
|
|
|
低溫脆化溫度
|
ASTM D-746
|
＜-76
|
℃
|